γ-Ray Irradiation-Derived MnO/rGO Composites for High Performance Lithium Ion Batteries
季恒星
Author NameAffiliationE-mail
季恒星 中国科学技术大学材料科学与工程系 jihengx@ustc.edu.cn 
Abstract:
We report a γ-ray irradiation reduction method to prepare MnO/reduced graphene oxide (rGO) nanocomposite for the anode of lithium ion batteries. γ-ray irradiation provide a clean way to generate homogeneously dispersed MnO nanoparticles with finely tuned size on rGO surface without the use of surfactant. The MnO/rGO composite enables a fully charge/discharge in 2 min to gain a reversible specific capacity of 546 mA h g-1 which is 45% higher than the theoretical value of commercial graphite anode.
Key words:  γ-ray irradiation reduction  MnO anode  Reduced graphene oxide  Nanocomposites  Lithium ion batteries
FundProject:
γ-射线辐照法制备氧化亚锰/石墨烯复合材料及其储锂性能研究
季恒星
摘要:
我们报道了一种γ-射线还原制备氧化亚锰/石墨烯复合材料的实验方法。该实验方法能够在不添加表面活性剂的条件下获得在溶剂中均匀稳定分散的氧化亚锰/石墨烯复合材料。其中氧化亚锰纳米粒子的生长速度可控制在0.8 nm h-1,因此可在避免表面活性剂的情况下实现氧化亚锰颗粒在石墨烯表面的尺寸调控和均匀分散。这些结构特征使得γ-射线还原法制备的氧化亚锰/石墨烯复合材料在用作储锂负极材料时展现出优异的倍率性能–2分钟充电可以获得高达546 mA h g-1的质量比容量(相对复合材料质量)
关键词:  γ-射线还原  氧化亚锰负极  石墨烯  纳米复合材料  锂离子电池