| Author Name | Affiliation | E-mail | | Ning Liu* | Department of Physics, Suzhou College, Suzhou 234000, China;Structure Research Laboratory, University of Science and Technology of China, Hefei 230026, China | liuning.szsz@ 163.com | | Guo-qing Yan | Department of Physics, Suzhou College, Suzhou 234000, China | | | Su-jun Xu | Structure Research Laboratory, University of Science and Technology of China, Hefei 230026, China | | | Wei Tong | Structure Research Laboratory, University of Science and Technology of China, Hefei 230026, China | |
|
| Abstract: |
| By measuring M-T curves, ρ-T curves and MR-T curves of the samples under different temperatures, the influence of Dy doping (0.00 ≤ x ≤0.30) on the magnetic and electric properties of La0.7-xDyxSr0.3MnO3 has been studied. The experimental results show that, with the increase of the Dy content, the system undergoes a transition from long range ferromagnetic order to the cluster-spin glass state and further to antiferromagnetic order. For the samples with x=0.20 and 0.30, their magnetic behaviors are abnormal at low temperature, and their resistivities at low temperature have a minimum value. These peculiar phenomena not only come from the lattice effect induced by doping, but also from extra magnetic coupling induced by doping.
|
| Key words: Manganite, Abnormality of resistivity at low temperature, Lattice effect, Extra magnetic coupling |
| FundProject: |
|
| La0.7-xDyxSr0.3MnO3(0.00≤x≤0.30)体系低温磁行为和电阻率的反常 |
|
刘宁*,严国清,徐素军,童伟
|
| 摘要: |
| 通过测量样品的磁化强度-温度曲线、电阻率-温度曲线及磁电阻-温度曲线,研究了Dy掺杂(0.00≤x≤0.30)对La0 7-xDyxSr0.3MnO3体系磁电性质的影响.实验发现,随Dy掺杂量的增加,体系磁结构从长程铁磁有序向自旋团簇玻璃态、反铁磁状态转变;x=0.20、0.30时的低温磁行为发生异常,电行为存在低温电阻率极小值现象.这些奇特现象不仅来源于掺杂引起的晶格效应,也来源于掺杂引起的额外磁性耦合.
|
| 关键词: 锰氧化物 低温电阻率反常 晶格效应 额外磁性耦合 |