All-Solid-State Thin Film Lithium Batteries with LiCoO2 Cathodes
Liu Wenyuan,Fu Zhengwen,Qin Qizong*
Author NameAffiliationE-mail
Liu Wenyuan Laser Chemistry Institute & Department of Chemistry, Shanghai Key Laboratory of Molecular Catalysts and Innovative Materials, Fudan University, Shanghai 200433  
Fu Zhengwen Laser Chemistry Institute & Department of Chemistry, Shanghai Key Laboratory of Molecular Catalysts and Innovative Materials, Fudan University, Shanghai 200433  
Qin Qizong* Laser Chemistry Institute & Department of Chemistry, Shanghai Key Laboratory of Molecular Catalysts and Innovative Materials, Fudan University, Shanghai 200433 qzqin@fudan.ac.cn 
Abstract:
Amorphous and oriented polycrystalline LiCoO2 thin films, used as cathode material for an all-solid-state thin film battery, were fabricated by using RF magnetron sputtering and annealed at different temperatures. The morphology and structure of LiCoO2 thin films were characterized by scanning electron microscopy and X-ray diffraction. All-solid-state thin film batteries, comprised of LiCoO2 cathode films with different structures, lithium phosphorous oxynitride electrolyte film and metallic lithium anode film, was successfully prepared and their properties were examined by chronopotentiometry. Results showed that the structure and crystallinity of the LiCoO2 films strongly influenced the electrochemical performance of all-solid-state thin film lithium batteries. Worth nothing was the battery with an oriented polycrystalline LiCoO2 film it exhibited the best electrochemical performance, and delivered a discharge capacity of ~55.4 μAh/cm2μm. Furthermore, when subjected to over 450 charge/discharge cycles, that battery suffered no obvious fode in capacity.
Key words:  LiCoO2, RF sputtering, LiPON, All-solid-state thin film lithium battery
FundProject:
以LiCoO2为阴极的全固态薄膜锂电池的研究
刘文元,傅正文,秦启宗*
摘要:
采用射频磁控溅射技术制备了非晶态和不同取向的多晶LiCoO2薄膜,利用XRD和SEM研究了不同温度退火后LiCoO2薄膜的结构和形貌.以具有不同结构的LiCoO2薄膜为阴极、含氮磷酸锂薄膜为电解质以及金属锂薄膜为阳极,成功地制备了电化学性能不同的全固态薄膜锂电池.由电化学研究结果表明, LiCoO2薄膜的结构和多晶取向决定了薄膜电池的电化学性能.采用具有一定取向的多晶LiCoO2薄膜制备的全固态薄膜锂电池具有最佳的性能,稳定放电容量达到55.4 μAh/cm2μm,充放电循环次数超过450次.
关键词:  LiCoO2  磁控溅射  LiPON  全固态薄膜锂电池
DOI:10.1088/1674-0068/18/6/1043-1047
分类号: