Investigation On the Behavior of Poly(acrylic acid) in Water Solution and Its Effect on the Rheology of α- Al2O3 Suspension
Lai Wei,Liu Xingqin
Author NameAffiliation
Lai Wei Solid State Chemistry & Inorganic Membrane Institute University of Science and Technology of China, Hefei 230026 
Liu Xingqin Solid State Chemistry & Inorganic Membrane Institute University of Science and Technology of China, Hefei 230026 
Abstract:
The influence of pH, relative molecular weight and concentration of poly(acrylic acid) (PAA) on the viscosity of PAA solution was investigated. It was found that the rheology of PAA solution was closely related to the ionization and conformation of PAA chains. The increasing rigidity and the stretching of polymer chain resulted in a maximum viscosity at pH=8. The viscosity change of PAAsolution with addition of alumina powder was studied. It was found that the suspension viscosity reached its minimum when the amount of ceramic powder and PAA was at a certain ratio. At the same time, the viscosity minimum was also influenced by the particle size of powder.
Key words:  Poly(acrylic acid), Suspension, Rheology
FundProject:国家自然科学基金资助项目.
聚丙烯酸水溶液及α-A12O3悬浮液的流变性研究
赖炜,刘杏芹
摘要:
研究了pH、聚丙烯酸(PAA)浓度和分子量对PAA水溶液的粘度的影响,发现溶液的流变行为与溶液中PAA高分子链的离子化程度和构型密切相关,高分子链刚性程度的增加和链的伸展使溶液在pH为7~9时的粘度最大;研究了在PAA溶液中引入陶瓷粉体后悬浮液的粘度变化,发现当陶瓷粉体和PAA的量达到一定比值时悬浮液体系的粘度达到最小值,同时发现陶瓷粉体的粒径大小与这一粘度最小值和悬浮液流变特性也有关.
关键词:  聚丙烯酸  悬浮液  流变行为