Preparation and Characterization of Magnetoplumbite Oxides CaNiyAl12-yO19-δ
Xu Zhanlin, Liu Yan, Li Wenxing, Bi Yingli, Zhen Kaiji
Department of Chemistry,Jilin University,Changchun 130023
Abstract:
A series of magnetoplumbite oxides CaNiyAl12-yO19-δ(y=0.3,0.6,0.9,1.0)were prepared and characterized using XRD,XPS,TPR and TGA techniques.The results showed that the series of oxides CaNiyAl12-yO19-δexhibited almost the same crystal structure and similar reduction stability.A pure magnetoplumbite oxidesCaNiyAl12-yO19-δ phase could be formed only when y value is at 0
Key words:  Magnetoplumbite oxides CaNiyAl12-yO19-*,Methane,CO2-reforming,Synthesisgas
FundProject:国家自然科学基金资助课题(批准号:29973012)
磁铅石型复合氧化物CaNiyAl12-yO19-δ的制备和性能表征
徐占林, 刘延, 李文兴, 毕颖丽, 甄开吉
吉林大学化学系催化研究室长春 130023
摘要:
制备了一系列磁铅石型复合氧化物CaNiyAl12-Yo19-δy=0.3,0.6,0.9,1.0),并用XRD、XPS、TPR和TGA技术对其结构和性能进行了表征。结果表明,该系列复合氧化物具有相同的晶体结构和相似的还原稳定性。当Ni调变量既0
关键词:  磁铅石型复合氧化物CaNiyAl12-yO19-*  甲烷;二氧化碳重整;合成气