Investigation of Phase Transition Process in PT/P[VDF(70)-TrFE(30)]Ferroelectric Composite by Using Thermally Stimulated Current Method
Peng Zhi,ZhangXingyuan,Zhou Yiqin,Zhang Jixiang
Author NameAffiliation
Peng Zhi Department of Polymer Science and Engineering,University of Science and Technology of China,Hefei 230026 
ZhangXingyuan Department of Polymer Science and Engineering,University of Science and Technology of China,Hefei 230026 
Zhou Yiqin Department of Chemistry,Qingdao University,Qingdao 266071 
Zhang Jixiang Department of Chemistry,Qingdao University,Qingdao 266071 
Abstract:
The thermally stimulated current(TSC)behaviors of PT/P[VDF(70)-TrFE(30)]composite were investigated systematically.Two kinds of the ferroelectric phase(less organized ferroelectric and organized ferroelectric phase)coexist in the copolymer matrix at room temperature.The phase transitions can be identified clearly by poling sample above the Curie point and then cooling it to different temperatures.The result shows that the para-to-ferroelec trictransitions on cooling appear at 62℃and 50℃,and ferro-to-paraelectric transitions on heating at about 95℃ and 108℃,respectively.It also indicates that traps exist in ferroelectric phase but not in paraelectric phase of the copolymer.Lead titanate(PT) does not contribute to the current peaks within the experimental temperature range,but it makes Tc decrease and causes the current density increase compared with the pure copolymer.
Key words:  P(VDF/TrFE) copolymer,Lead titanate,Ferroelectric transition,Thermally stimulated current
FundProject:国家自然科学基金资助项目
钛酸铅与偏氟乙烯-三氟乙烯共聚物形成的铁电复合物相变过程的热释电研究
彭智,张兴元,周漪琴,章吉祥
摘要:
研究了偏氟乙烯-三氟乙烯共聚物与钛酸铅形成的铁电复合物PT/P[VDF(70)-TrFE(30)]的热释电流行为。P[VDF(70)-TrFE(30)]室温下存在两个铁电相,即较无序的铁电相和较有序的铁电相,升温经过各自的相转变点后转变成较有序的顺电相和较无序的顺电相。热释电流谱上出现在95℃和108℃的两个电流峰,分别由两个铁电相的结构陷阱以及部分取向的偶极所贡献。采用Tc以上温度极化并冷却到不同温度的方法可明确鉴别出该试样两个顺电相降温转变过程,转变点分别为62℃和50℃。实验证实陷阱仅存在于铁电相而
关键词:  偏氟乙烯-三氟乙烯共聚物  钛酸铅  铁电相变  热释电流