| Author Name | Affiliation | E-mail | | Shen Ning | Department of Chemical Physics, Lab of Biomass Clean Energy, University of Science and Technology of China, Hefei 230026, China | | | Jing Shen | Department of Chemical Physics, Lab of Biomass Clean Energy, University of Science and Technology of China, Hefei 230026, China | | | Xing-long Li | Department of Chemical Physics, Lab of Biomass Clean Energy, University of Science and Technology of China, Hefei 230026, China | | | Quan-xin Li* | Department of Chemical Physics, Lab of Biomass Clean Energy, University of Science and Technology of China, Hefei 230026, China | liqx@ustc.edu.cn |
|
| Abstract: |
| We provides a novel approach to generate low-temperature atomic oxygen anions (O-) emis-sion using the cesium oxide-doped 12CaO·7Al2O3 (Cs2O-doped C12A7). The maximal emis-sion intensity of O- from the Cs2O-doped C12A7 at 700 oC and 800 V/cm reached about 0.54 μA/cm2, which was about two times as strong as that from the un-doped C12A7(0.23 μA/cm2) under the same condition. The initiative temperature of the O- emission from the Cs2O-doped C12A7 was about 500 oC, which was also much lower than the initiative temperature from the un-doped C12A7 (570 oC) in the given field of 800 V/cm. High pure O- emission close to 100% could be obtained from the Cs2O-doped C12A7 under the lower temperature (<550oC). The emission features of the Cs2-doped C12A7, including the emis-sion distribution, temperature effect, and emission branching ratio have been investigated in detail and compared with the un-doped C12A7. The structure and storage characteristics of the resulting material were also investigated via X-ray diffraction and electron paramag-netic resonance. It was found that doping Cs2 to C12A7 will lower the initiative emission temperature and enhance the emission intensity. |
| Key words: Atomic oxygen anion, Cs2O-doped C12A7, Emission characteristics, Storage characteristics |
| FundProject: |
|
| 掺杂Cs2O的12CaO·7Al2O3型发射材料的制备与特性 |
|
宁珅,沈静,李兴龙,李全新*
|
| 摘要: |
| 研究了掺杂Cs2O的12CaO·7Al2O3(C12A7)型负离子存储发射材料的发射特性、离子发射分支比以及温度对发射强度的影响，同时对该材料的X射线衍射和电子顺磁共振的表征结果进行了分析. C12A7中Cs2O的掺入不仅降低了发射温度，同时还增强了发射强度. 掺杂Cs2O后，在800 V/cm的引出场下，发射温度由570 oC降低至500 oC，在700 oC时，发射强度由0.23 μA/cm< |
| 关键词: 氧负离子，Cs2O掺杂，C12A7，存储特性，发射特性 |
| DOI：10.1088/1674-0068/24/03/335-339 |