Oxygen Nonstoichiometry and Permeability of Co-substituted YBa2Cu3O6+δ

Funds:  Project supported by the National Natural Science Foundation of China (50225208).
  • Received Date: 2003-06-05
  • The effects of substitution of Cu by Co in YBa2Cu3O6+δ on the oxygen nonstoichiometry and permeability were investigated. The oxygen nonstochiometry δ increased as a result of Co substitution, and its values did not change very much with the changing temperature and oxygen partial pressure. An oxygen permeation flux of 57 μmol/cm2s was observed at 850℃ from YBa2Cu2CoO6+δ disk-shaped dense sample of thickness 1.2 mm with one side exposed to air (PO2=21.2 kPa) and the other side to flowing helium (PO2=101 Pa), but only 31 μmol/cm2s was measured for YBa2Cu3O6+δ. The improved oxygen permeabilty in YBa2Cu2CoO6+δ was attributed to the even distribution of oxygen ions and oxygen vacancacies in the basal plane.
  • 加载中
  • 加载中
通讯作者: 陈斌, bchen63@163.com
  • 1. 

    沈阳化工大学材料科学与工程学院 沈阳 110142

  1. 本站搜索
  2. 百度学术搜索
  3. 万方数据库搜索
  4. CNKI搜索

Article Metrics

Article views(874) PDF downloads(936) Cited by()

Proportional views
Related

Oxygen Nonstoichiometry and Permeability of Co-substituted YBa2Cu3O6+δ

Funds:  Project supported by the National Natural Science Foundation of China (50225208).

Abstract: The effects of substitution of Cu by Co in YBa2Cu3O6+δ on the oxygen nonstoichiometry and permeability were investigated. The oxygen nonstochiometry δ increased as a result of Co substitution, and its values did not change very much with the changing temperature and oxygen partial pressure. An oxygen permeation flux of 57 μmol/cm2s was observed at 850℃ from YBa2Cu2CoO6+δ disk-shaped dense sample of thickness 1.2 mm with one side exposed to air (PO2=21.2 kPa) and the other side to flowing helium (PO2=101 Pa), but only 31 μmol/cm2s was measured for YBa2Cu3O6+δ. The improved oxygen permeabilty in YBa2Cu2CoO6+δ was attributed to the even distribution of oxygen ions and oxygen vacancacies in the basal plane.

Zheng Cuihong, Yang Pinghua, Liu Wei, Chen Chusheng. Oxygen Nonstoichiometry and Permeability of Co-substituted YBa2Cu3O6+δ[J]. Chinese Journal of Chemical Physics , 2003, 16(6).
Citation: Zheng Cuihong, Yang Pinghua, Liu Wei, Chen Chusheng. Oxygen Nonstoichiometry and Permeability of Co-substituted YBa2Cu3O6+δ[J]. Chinese Journal of Chemical Physics , 2003, 16(6).

Catalog

    /

    DownLoad:  Full-Size Img  PowerPoint
    Return
    Return