Liu Wei, Deng Zengqiang, Zhang Xiao, Jin Xin, Chen Chusheng. Defects Formation and Transportation Process Study of Mixed Conductor La1-xSrxCoO3-δ[J]. Chinese Journal of Chemical Physics , 2000, 13(5): 599-604. doi: 10.1088/1674-0068/13/5/599-604
Citation: Liu Wei, Deng Zengqiang, Zhang Xiao, Jin Xin, Chen Chusheng. Defects Formation and Transportation Process Study of Mixed Conductor La1-xSrxCoO3-δ[J]. Chinese Journal of Chemical Physics , 2000, 13(5): 599-604. doi: 10.1088/1674-0068/13/5/599-604

Defects Formation and Transportation Process Study of Mixed Conductor La1-xSrxCoO3-δ

doi: 10.1088/1674-0068/13/5/599-604
  • Received Date: 1999-06-30
  • The average valence of Co ions and the oxygen nonstochiometry of perovskite-type oxides La1-xSrxCoO3-δwere studied by meansof iodometric titration. It hasbeen found that the cobalt valence increases with the strontium content, goes through a maximum atx=0.5 and decreases with higher strontium content. At room temperature, the maximum appears atx=0.5, and it shifts tox=0.4 when the temperature increases. Theelectrical conductivity and relaxationstrengthof internal friction peak at 330K shows the similar variation pattern. For the same Sr dopant content, the average valence of Co decreases with the temperature.
  • 加载中
  • 加载中
通讯作者: 陈斌, bchen63@163.com
  • 1. 

    沈阳化工大学材料科学与工程学院 沈阳 110142

  1. 本站搜索
  2. 百度学术搜索
  3. 万方数据库搜索
  4. CNKI搜索

Article Metrics

Article views(1212) PDF downloads(1290) Cited by()

Proportional views
Related

Defects Formation and Transportation Process Study of Mixed Conductor La1-xSrxCoO3-δ

doi: 10.1088/1674-0068/13/5/599-604

Abstract: The average valence of Co ions and the oxygen nonstochiometry of perovskite-type oxides La1-xSrxCoO3-δwere studied by meansof iodometric titration. It hasbeen found that the cobalt valence increases with the strontium content, goes through a maximum atx=0.5 and decreases with higher strontium content. At room temperature, the maximum appears atx=0.5, and it shifts tox=0.4 when the temperature increases. Theelectrical conductivity and relaxationstrengthof internal friction peak at 330K shows the similar variation pattern. For the same Sr dopant content, the average valence of Co decreases with the temperature.

Liu Wei, Deng Zengqiang, Zhang Xiao, Jin Xin, Chen Chusheng. Defects Formation and Transportation Process Study of Mixed Conductor La1-xSrxCoO3-δ[J]. Chinese Journal of Chemical Physics , 2000, 13(5): 599-604. doi: 10.1088/1674-0068/13/5/599-604
Citation: Liu Wei, Deng Zengqiang, Zhang Xiao, Jin Xin, Chen Chusheng. Defects Formation and Transportation Process Study of Mixed Conductor La1-xSrxCoO3-δ[J]. Chinese Journal of Chemical Physics , 2000, 13(5): 599-604. doi: 10.1088/1674-0068/13/5/599-604

Catalog

    /

    DownLoad:  Full-Size Img  PowerPoint
    Return
    Return