Xiao Zhang, Xing-ping Zhou, Si-yu Ni, Guo-liang Dai, Yin-sheng Wang. Preparation and Optical Properties of CdTe/CdO-nH2O Core/shell Nano-composites in Aqueous Solution[J]. Chinese Journal of Chemical Physics , 2007, 20(6): 779-783. doi: 10.1088/1674-0068/20/06/779-783
Citation: Xiao Zhang, Xing-ping Zhou, Si-yu Ni, Guo-liang Dai, Yin-sheng Wang. Preparation and Optical Properties of CdTe/CdO-nH2O Core/shell Nano-composites in Aqueous Solution[J]. Chinese Journal of Chemical Physics , 2007, 20(6): 779-783. doi: 10.1088/1674-0068/20/06/779-783

Preparation and Optical Properties of CdTe/CdO-nH2O Core/shell Nano-composites in Aqueous Solution

doi: 10.1088/1674-0068/20/06/779-783
Funds:  This work was supported by the Shanghai Municipal 2006 Nanometer Special Project (No.0652nm008).
  • Received Date: 2007-08-30
  • Rev Recd Date: 2007-09-10
  • "The deposition of CdO?nH2O on CdTe nanoparticles was studied in an aqueous phase. The CdTe nanocrystals (NCs) were prepared in aqueous solution through the reaction between Cd2+ and NaHTe in the presence of thioglycolic acid as a stabilizer. The molar ratio of the Cd2+ to Te2- in the precursory solution played an important role in the photoluminescence of the ultimate CdTe NCs. The strongest photoluminescence was obtained under 4.0 of [Cd2+]/[Te2-] at pH?8.2. With the optimum dosage of Cd(II) hydrous oxide deposited on the CdTe NCs, the photoluminescence was enhanced greatly. The photoluminescence of these nanocomposites was kept constant in the pH range of 8.0-10.0, but dramatically decreased with an obvious blue-shifted peak while the pH was below 8.0. In addition, the photochemical oxidation of CdTe NCs with cadmium hydrous oxide deposition was markedly inhibited."
  • 加载中
  • 加载中
通讯作者: 陈斌, bchen63@163.com
  • 1. 

    沈阳化工大学材料科学与工程学院 沈阳 110142

  1. 本站搜索
  2. 百度学术搜索
  3. 万方数据库搜索
  4. CNKI搜索

Article Metrics

Article views(1850) PDF downloads(1376) Cited by()

Proportional views
Related

Preparation and Optical Properties of CdTe/CdO-nH2O Core/shell Nano-composites in Aqueous Solution

doi: 10.1088/1674-0068/20/06/779-783
Funds:  This work was supported by the Shanghai Municipal 2006 Nanometer Special Project (No.0652nm008).

Abstract: "The deposition of CdO?nH2O on CdTe nanoparticles was studied in an aqueous phase. The CdTe nanocrystals (NCs) were prepared in aqueous solution through the reaction between Cd2+ and NaHTe in the presence of thioglycolic acid as a stabilizer. The molar ratio of the Cd2+ to Te2- in the precursory solution played an important role in the photoluminescence of the ultimate CdTe NCs. The strongest photoluminescence was obtained under 4.0 of [Cd2+]/[Te2-] at pH?8.2. With the optimum dosage of Cd(II) hydrous oxide deposited on the CdTe NCs, the photoluminescence was enhanced greatly. The photoluminescence of these nanocomposites was kept constant in the pH range of 8.0-10.0, but dramatically decreased with an obvious blue-shifted peak while the pH was below 8.0. In addition, the photochemical oxidation of CdTe NCs with cadmium hydrous oxide deposition was markedly inhibited."

Xiao Zhang, Xing-ping Zhou, Si-yu Ni, Guo-liang Dai, Yin-sheng Wang. Preparation and Optical Properties of CdTe/CdO-nH2O Core/shell Nano-composites in Aqueous Solution[J]. Chinese Journal of Chemical Physics , 2007, 20(6): 779-783. doi: 10.1088/1674-0068/20/06/779-783
Citation: Xiao Zhang, Xing-ping Zhou, Si-yu Ni, Guo-liang Dai, Yin-sheng Wang. Preparation and Optical Properties of CdTe/CdO-nH2O Core/shell Nano-composites in Aqueous Solution[J]. Chinese Journal of Chemical Physics , 2007, 20(6): 779-783. doi: 10.1088/1674-0068/20/06/779-783

Catalog

    /

    DownLoad:  Full-Size Img  PowerPoint
    Return
    Return