Synthesis and Electrorheological Properties of LTNO-PS Composites

Core-shell structural Li and Ti co-doped NiO/polystyrene samples (LTNO/PS) were synthesized by a sol-gel method and studied by TEM, X-ray diffraction, IR spectroscopy and LCR meter. It was found that the core-shell LTNO/PS particles are nearly smooth spheres with an average size of around 4.0 mm, while the LTNO particles alone have a size of around 3.5 mm. The electrorheological activity of LTNO particles with PS coating is larger than that of the bare ones with the same components. This research reveals that the high dielectric constant and corresponding dielectric loss of the LTNO is related to the Li and Ti contents. The increase of electrorheological activity of LTNO particles with PS coating is caused by the increase of dielectric permittivity, the surface structural change, and the reduction of leakage current of PS-coated samples due to the high resistivity and soft contacting of PS shell. By the preparation of core/shell structural materials and taking the advantage of the shell to reduce the leakage current between the particles, the electrorheological effect can be effectively increased.