Impact of Eu³⁺ Ions on Physical and Optical Properties of Li₂O-Na₂O-B₂O₃ Glass

The lithium sodium borate glasses doped with Eu³⁺ ion are prepared using melt quenching technique, their structural and optical properties have been evaluated. The density of prepared glasses exhibits an inverse behavior to the molar volume ranging from 2.26 g/cm³ to 2.43 g/cm³ and 26.95 cm³ /mol to 26.20 cm³ /mol, respectively. The absence of sharp peaks in XRD patterns confirms the amorphous nature of the prepared glasses. The absorption spectra yield four transitions centered at 391 nm (⁷F₀→⁵L₆), 463 nm (⁷F₀→⁵D₂), 531 nm (⁷F₀→⁵D₁), and 582 nm (⁷F₀→⁵D₀). The most intense red luminescence is observed at 612 nm corresponding to ⁵D₀→⁷F₂ transition under 390 nm laser excitations.